请教焊接残余应力的一个问题

meiyuxx

我用ANSYS计算焊接残余应力时,发现不同的参考温度,残余变形和残余应力会不同.比如参考温度设为25度,假设焊缝升温到1200度,然后空冷到30度,发现整个焊件并没有缩短.如果参考温度为1200,缩短很多。不知道求残余应力和变形时,参考温度如何设置.希望哪位大侠帮我分析一下.多谢.我的QQ26216882.

StaDency

Defines the reference temperature for the thermal strain calculations in structural analyses. Thermal strains are given by  a *(T-TREF), as explained in Section 2.1 of the ANSYS Theory Reference, where a is the coefficient of thermal expansion material property and T is the element temperature. Units should be consistent with a .

Reference temperatures may also be input per material by using the label REFT on the material property [MP] command, such as MP,REFT,MAT,C0. Only a constant (non-temperature-dependent) value is allowed. The value input on the TREF command applies to all materials not having a specified material property definition.

HELP里的说明，与延展率相关，strain= a *(T-TREF)也可通过材料属性编辑。 不知道你材料属性给出到什么程度。
材料各种属性随温度变化线性/非线性，属性与温度对应，当然影响了。

dpecysl

参考温度设为25度,假设焊缝升温到1200度,然后空冷到30度,最终温差30-25度，比参考温度升5度。

如果参考温度为1200,也空冷到30度，最终温差30-1200度，比参考温度降1170度。

都以参考温度为准，热胀冷缩的结果当然差很多。

仅供参考。

zlj

参考温度设为环境温度,25度是合理的,冷却到30度可以得到合理的结果,如果结果有问题,因该不是因为参考温度.