算冲击问题得到结果比文献里面小请问k文件应该怎么改？

wq2013

k文件附上，模型和材料都和文献里面一样
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$                             SECTION DEFINITIONS                              $
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$
*SECTION_SOLID
         1         1
$
$
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$                             MATERIAL DEFINITIONS                             $
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$
*MAT_JOHNSON_COOK
         1   4.51E-9     42481    113000      0.33
      1130       250       0.2     0.032         1      1920       293         1
563000000         0      3.00       0.0         0      0.33      0.48     0.004         
       3.9   
*EOS_GRUNEISEN
         1   5130000     1.028      0.00      0.00      1.23         0      0.00   
      1.00   
*MAT_JOHNSON_COOK
         2   7.82E-9     76923    200000       0.3
       507       320      0.28     0.064      1.06      1783       293         1
465000000         0      3.00       0.0       0.1      0.76      1.57     0.005         
     -0.84   
*EOS_GRUNEISEN
         2   4569000      1.49      0.00      0.00      2.17      0.46      0.00   
      1.00   
$
$
$
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$                              PARTS DEFINITIONS                               $
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$
$
*PART
Part          1 for Mat         1 and Elem Type         1
         1         1         1         1         0         0         0
$
*PART
Part          2 for Mat         2 and Elem Type         1
         2         1         2         2         0         0         0
$
$
。。。。。。
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$                              CONTACT DEFINITIONS                             $
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$
*CONTACT_ERODING_SURFACE_TO_SURFACE
         2         1         3         3         0         0         0         0
    0.1500    0.1500     0.000     0.000     0.000         0      
     1.000     1.000     0.000     0.000     1.000     1.000     1.000     1.000  
         1         1         1
$
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$                              CONTROL OPTIONS                                 $
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$
*CONTROL_ENERGY
         2         2         2         2
*CONTROL_BULK_VISCOSITY
  1.50     0.600E-01
*CONTROL_CONTACT
       0.5   1.00000         
   
*CONTROL_TIMESTEP
    0.0000    0.9000         0  0.00      0.00   
*CONTROL_TERMINATION
    0.0016         0   0.00000   0.00000   0.00000
$
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$                                 TIME HISTORY                                 $
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$
*DATABASE_BINARY_D3PLOT
   0.00004
*DATABASE_BINARY_D3THDT
   0.00004
$
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$                              DATABASE OPTIONS                                $
$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$$
$
*DATABASE_EXTENT_BINARY
         0         0         3         1         0         0         0         0
         0         0         4         0         0         0
*INITIAL_VELOCITY_GENERATION
         2         2                       -200000   
*LOAD_THERMAL_CONSTANT
         0
698.0           
*END

pengyong

是接触刚度，这个有一定影响。
如果你只是要重现文献里的例子，首先要仔细对比下材料模型以及EOS是不是和文献一致，单位系统相不相同。另外检查下网格尺寸是不是和文献一致。。
如果还不一样，就没必要纠结和文献对比了，找一个其它的有源K文件的例子做一下就行

交大车辆

上传一个.k文件，这样看格式乱掉了，头疼。

wq2013

交大车辆 发表于 2017-5-7 23:56
上传一个.k文件，这样看格式乱掉了，头疼。

你好，k文件太大了上传不上去，能不能加个qq呢我发给你，麻烦了，我的qq3069518317

wq2013

交大车辆 发表于 2017-5-7 23:56
上传一个.k文件，这样看格式乱掉了，头疼。

https://pan.baidu.com/s/1dEPr3PJ
你好我把k文件放到网盘里面了，应该可以看

pengyong

先调*CONTROL_CONTACT，不行再调*MAT_JOHNSON_COOK里参数

wq2013

pengyong 发表于 2017-5-10 21:08
先调*CONTROL_CONTACT，不行再调*MAT_JOHNSON_COOK里参数

你好，jc本构的参数是取得文献里面的，contral—contact是调整接触刚度吗？谢谢啦

wq2013

pengyong 发表于 2017-5-11 09:39
是接触刚度，这个有一定影响。
如果你只是要重现文献里的例子，首先要仔细对比下材料模型以及EOS是不是和文 ...

谢谢你了，我在试试

交大车辆

你说的是什么结果比文献小？