复合材料冲击损伤模拟general contact surface has coincident nodes

rufeng020802 · 发表于 2011-6-9 23:54:14

本帖最后由 zsq-w 于 2011-6-10 07:53 编辑

用体单元建模，考虑移除失效单元后的内部单元接触，按robert_su兄的方法设置后，计算出现以下错误：
A facet that is part of a general contact surface has coincident nodes. A facet with coincident nodes cannot be part of a general contact surface. See nodes 663 and 7763 on element 4801 of instance PLATE-1. Please check the nodal coordinates of nodes of this element. Also, please check if these nodes are slave nodes in a *TIE definition. Adjusting the slave node coordinates of improperly defined *TIE definitions may cause excessive distortions of the underlying elements resulting in collapsed facets. If the nodes are slave nodes in a *TIE definition, please check the *TIE definition for consistency, making sure that there are no common nodes between the slave and master surfaces.
请问怎么解决？谢谢。

rufeng020802 · 发表于 2011-6-10 11:47:09

求指点。。。

ypyae86 · 发表于 2011-6-10 12:53:24

你是不是层与层之间加粘性层了，是因为粘性层的原因，因为粘性层是上下面节点重合的六面体单元，无法用于general contact中，去掉粘性层或者不采用删除单元的方法，接触只定义到表面，不要涉及到粘性层，不知道你是否有更好的解决办法，期待你有更好的方法，我也想学习！

rufeng020802 · 发表于 2011-6-12 10:37:15

3# ypyae86
那就是如果用粘性层的话，robert_su的那种考虑移除失效单元后的内部单元接触的设置方法就不适用了？这样的话，接触应该怎样设置呢？求高手指点，谢谢。

ypyae86 · 发表于 2011-6-12 22:17:19

对的，现在我也不会，我只能把粘性层拿掉，将分层的应力更新在子程序中体现出来。

rufeng020802 · 发表于 2011-6-12 22:51:31

5# ypyae86

那复合材料接触怎么设置，用通用接触还是面面接触？难道层与层之间也设置接触？

rufeng020802 · 发表于 2011-6-15 09:54:49

求高手指点。

hanmeng · 发表于 2020-10-15 10:36:12

同问，有人知道怎么解决吗